Abstract
End of life photovoltaic panels of different technologies (poly crystalline Si, amorphous Si, and CdTe) were treated mechanically in pilot scale by single shaft shredder minimizing the production of fine fractions below 0.4 mm (<18% weight). Grounded material was sieved giving: an intermediate fraction (0.4–1 mm) of directly recoverable glass (18% weight); a coarse fraction (which should be further treated for encapsulant removal), and fine fractions of low-value glass (18%), which can be treated by leaching for the removal of metal impurities. Encapsulant removal from coarse fraction was successfully performed by solvent treatment using cyclohexane at 50 °C for 1 h giving high-grade glass (52% weight), which can be reused for panel production. Experimental results of solvent treatment were compared with those from thermal treatment by economic analysis and Life Cycle Assessment, denoting in both cases the advantages of solvent treatment in recovering high-value glass.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.