Abstract

Mechanochemistry enables rapid, quantitative reactions to occur at or close to 27℃. It is a one-step process that allows for reactant homogenization, product nucleation, and particle growth. These processes use little or no solvent, making them less wasteful and more environmentally friendly than solvent-based reactions. Ni2+ , Mn2+, Cr2+and Cu2+ metal ions were synthesized by grinding in an agate mortar with pestle using ligands derived from amino acids (Histidine &Alanine) which were further synthesized to form complexes. The entire experiment was carried out by solvent solvent-assisted mechanochemical process and ethanol was used as liquid liquid-assisted solvent. The complexes were characterized by IR spectroscopy, U-V spectroscopy, X-ray analysis, melting point, solubility test, and conductivity measurement. The Solubility test showed that the complexes are soluble in DMSO, DMF, and ethanol and are insoluble in both hexane and tetrachloromethane. The molar conductivity values are in the range of (6.05-28.56) Ω-1cm2mol-1 ) indicating the complexes behave as non-electrolytes. IR analysis showed a vibrational frequency band observed at (1620-1625) cm-1 which is assigned to the ʋ(C=N) of the azomethine, also the new bands M=N, M=O indicate the coordination reaction between the metal and the ligands. The UV visible analysis shows various transitions, the metal complexes showed adsorption bands at λ of 420 and 575nm respectively because of the ligand-to-metal charge transfer (LMCT). The XRD analysis showed that there was a change in phase between the starting material and the product which indicate that a reaction occurred, also the nature of the spectra showed that the compounds are all crystalline. The Antimicrobial activity showed that both the complexes and the ligands have good activity against the bacterial isolates. Antioxidant activity was also tested and the compound appeared to have moderate scavenging activities compared to the reference used. The values indicated that the activities are more pronounced when coordinated with metal ions.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.