Abstract
Two different multimetal organic compounds were synthesized and used to deposit thin Y:Ba:Cu oxide films on selected metal and ceramic substrates by the dip‐coating method. The rheology of the precursors is strongly influenced by the organic ligand, types of solvent, solvent–water molar ratio, and processing method. The precursor compounds were converted to suitable viscosity to achieve uniform film thickness processing on complex geometry. Superconducting transition temperatures Tc in the range of 89 to 93 K have been measured, depending on processing parameters used. The critical current density, Jc of the solution‐coated films had values comparable to those for poly‐crystalline samples. Y123 films exhibit c‐axis alignment on Ag substrates. A prototype high‐Q cavity was coated with Y123 and its performance was evaluated.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.