Abstract
The Ca(ZrxTi1−x)O3 ceramic was prepared by solid state reaction method. Structural characterizations were performed by means of XRD, FT-Raman and FTIR. The formation of monophasic compounds obtained in the composition x=0.0–0.2 and 0.9–1.0 were confirmed from XRD, FT-Rama and FTIR spectroscopy. However the compositions between x=0.3 and 0.8 showed presence of mixed phase or secondary phase. The microwave dielectric constant, Q×f and τf changed from 158 to 141, 4321 to 5945 and from 843.9 to 732.33ppm/°C respectively in the composition between x=0.0 and 0.2. The anomalous results of dielectric constant, Q×f and τf values in the composition between x=0.3 and 0.8 were observed. The microwave dielectric constant and τf were found to be decreased from 42 to 27 and 81.75 to −19.98ppm/°C in the composition between x=0.9 and 1.0 respectively. The Q×f values increased from 10728 to 16543 with the increase of x value from 0.9 to 1.0. The dielectric resonator antenna (DRA) was investigated experimentally and numerically using a monopole antenna through an infinite ground plane and Ansoft’s high frequency structure simulator software, respectively. The required resonance frequency and bandwidth of DRA were investigated in the composition between 0≤x≤1.0.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.