Solubility and partial molar volume of carbon dioxide and ethane in crosslinked poly(ethylene oxide) copolymer

Abstract

AbstractExperimental solubility and sorptive dilation data are reported for carbon dioxide and ethane in a crosslinked poly(ethylene oxide) (XLPEO) rubbery copolymer. Five different temperatures (253 ≤ T(K) ≤ 308) were considered, with a maximum gas pressure of 2.09 MPa (20.6 atm). The polymer was prepared by photopolymerization of a solution containing 70 wt % poly(ethylene glycol) methyl ether acrylate (PEGMEA) and 30 wt % poly(ethylene glycol) diacrylate (PEGDA). Sorption isotherms were described by the Flory‐Huggins model. For each gas, the Flory‐Huggins interaction parameter was a decreasing function of temperature and did not show a composition dependence. Dilation and sorption data were combined to calculate the partial molar volume (PMV) of the gases in the polymer, which was an increasing function of temperature. Based on a comparison with literature data for a XLPEO homopolymer prepared from pure PEGDA over the same range of operating conditions, an effect of the network composition on both gas solubility and PMV was found. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 456–468, 2010