Solid-State Metalized Reduction of Magnesium-Rich Low-Nickel Oxide Ores Using Coal as the Reductant Based on Thermodynamic Analysis

Abstract

The solid-state metalized reduction of magnesium-rich low-nickel oxide ore using coal as a reductant was studied based on thermodynamic analysis. The major constituent minerals of the ore were silicates and goethite. The former was the main nickel-bearing mineral, and the latter was the main iron-bearing mineral. Single factor tests were conducted to investigate the effects of reduction temperature, duration, and coal dosage on the beneficiation of nickel and iron such that optimal conditions were achieved. Considering the low recoveries of nickel and iron (Ni, 13.9 pct; Fe, 30.3 pct) under the obtained optimal conditions, an improved process, adding CaF2 before the reaction, was proposed to modify the solid-state metalized process. The results showed that the recoveries of nickel and iron reached to 96.5 and 73.4 pct, respectively, and that the grades of nickel and iron in the concentrate increased from 2.5 and 62.6 wt pct to 6.9 and 71.4 wt pct, respectively. Nickel and iron in the absence of CaF2 were metalized; nevertheless, the size of ferronickel particles was only 1 μm. Furthermore, alloys in the presence of CaF2 aggregated and exhibited bands with a length greater than 200 µm. These observations suggested that CaF2 could effectively reduce the surface tension of the newly generated alloy interface and promote the migration and polymerization of the alloy particles, which improves the beneficiation of nickel and iron by magnetic separation.