Abstract
Solidification of Coal Fly-ash (CFA) has been carried out using a hydrothermal processing method. In the hydrothermal processing, the CFA was first compacted in a mold at 20 - 50 MPa, and then hydrothermally cured in an autoclave. The hydrothermal curing was performed at 150 – 250°C for 15 – 60 h. The experimental results showed that NaOH solution, Ca(OH)2 content, compaction pressure, autoclave curing temperature and time significantly affected the strength of solidified bodies. The most important strength-producing constituent in the solidified bodies produced with CFA was tobermorite, or tobermorite-like calcium silicate hydrate. When the CaO/SiO2 ratio of the starting material was close to 0.83, tobermorite readily formed and the formed tobermorite enhanced the strength of solidified bodies. The tensile strength determined by the Brazilian test reached more than 10 MPa under the hydrothermal processing. As such, the hydrothermal processing method may provide a high potential for recycling CFA on a large scale.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.