Abstract
Abstract It has been reported that solidification of the Al2O3–YAG equilibrium eutectic structure follows melting of the Al2O3–YAP metastable eutectic structure. Since the exothermic heat due to solidification was consumed by the endothermic heat due to melting, a fine and uniform eutectic structure was obtained. However, the composition of the Al2O3–YAG eutectic structure is restricted to the metastable eutectic composition. In this paper, Al2O3–YAG eutectic compacts with an off-metastable eutectic composition were prepared by the addition of Al2O3 particles to Al2O3–YAP eutectic particles with diameters less than 20 μm. In compositions ranging from 18.5 mol%Y2O3 to 13.5 mol%Y2O3, dense Al2O3–YAG eutectic compacts were formed without any Al2O3 segregation. The flexural strength and the fracture toughness remained almost unchanged with the increase in the Al2O3 phase. The addition of Al2O3 particles to the Al2O3–YAP eutectic particles enabled the matrix phase to change from the YAG phase to the Al2O3 phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.