Abstract
The intermetallic cadmium compounds LaPdCd2 and PrNi0.951(4)Cd2 were synthesized from the elements in sealed tantalum tubes in an induction furnace. Both phases were investigated by X-ray diffraction on powders and single crystals: MgCuAl2-type, Cmcm, Z = 4, a = 431.9(1), b = 1015.7(4), c = 835.7(2) pm, wR2 = 0.0436, 326 F2 values, 16 variables for LaPdCd2 and a = 420.26(8), b = 981.0(2), c = 815.3(1) pm, wR2 = 0.0404, 604 F2 values, 17 variables for PrNi0.951(4)Cd2. A small nickel deficit was observed for the PrNi0.951(4)Cd2 crystal. The cadmium atoms build up orthorhombically distorted three-dimensional networks (Cd-Cd distances: 302 - 334 pm) that resemble the structure of hexagonal diamond, lonsdaleite. Together with the palladium (nickel) atoms, [PdCd2] and [Ni0.951(4)Cd2] networks are formed which leave distorted hexagonal channels for the rare earth atoms.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.