Abstract
Comparative study of reactivity of nano- and micro-sized alumina and nickel oxide, obtained by the electrical explosion of metal wires in oxidizing atmosphere, was carried out for the reactions NiO + MoO 3, NiO + Al 2O 3, and Al 2O 3 + Bi 2O 3 by coupled anneals of ceramics, measurements of the conductivity of individual oxides and raw oxide mixtures, X-ray diffraction and differential thermal analysis. The total conductivity of nano-structured oxides was found lower than that of micro-structured ceramics. Mixing bismuth oxide with nano-structured alumina leads to stabilization of the low temperature polymorph α-Bi 2O 3 up to 780 °C. The diffusion permeability of NiMoO 4 layer grown at the surface of NiO ceramics, having submicron grains, was found 2 times lower if compared to NiMoO 4 grown at micro-sized NiO ceramics. NiO and Al 2O 3 nano-powders preserve the high reactivity even when heated up to 1000 °C. The results are discussed in terms of size effects on the solid state reactivity of oxides.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.