Abstract
In the present study, solid particle erosion resistance of high-velocity oxy-fuel (HVOF)-sprayed WC-CoCr coatings was evaluated. Erosion testing was conducted using alumina (Al2O3) powder as the erodent with three different impact angles (30, 60, and 90°) and impact velocity was kept constant. The coatings were deposited using two different powders; one was composed of conventional WC particles and second one contained nanoscale particles mixed with CoCr binder material. Erosion testing was carried out at room temperature using an air-jet erosion test setup. The effect of varying impact angles was studied and discussed with the help of scanning electron microscopy images of worn surfaces of coatings. The results showed that coating properties like microhardness and fracture toughness have a strong influence on the erosion behavior. During erosion testing, material was removed by fracturing and pullout of WC grains from the binder matrix. The morphology of the eroded surface also showed cutting, lip, and groove formation in the binder matrix caused by the repetitive impacts of erodent particles. It was observed that coating with nano-WC grains exhibited higher erosion resistance compared to conventional coating.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.