Abstract
NiO/ZrO2-Y2O3 (NiO/YSZ) anode functional layers (AFL) with 16-60 vol.% of NiO were deposited onto NiO/YSZ anode substrates by magnetron sputtering, followed by annealing in air at 1200 °C. The optimal deposition conditions for NiO/YSZ were determined. NiO content in the films was varied by changing the oxygen flow rate during the sputtering process. The microstructure and phase composition of NiO/YSZ anode functional layer were studied by SEM and XRD methods. Anode functional layers were fully crystallized and comprised of grains up to 500 nm in diameter after reduction in hydrogen. Anode-supported solid oxide fuel cells (SOFC) with the diameter of 20 mm including the magnetron sputtered AFL, 4-microns thick YSZ electrolyte and La0.6Sr0.4Co0.2Fe0.8O3/Ce0.9Gd0.1O2 (LSCF/CGO) cathode were fabricated and tested. Electrochemical properties of the single fuel cells were investigated as a function of NiO volume content in AFL and AFL thickness.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.