Abstract
AbstractComposite powders containing titanium diboride and boron carbide have been prepared by sol‐gel method at 1450°C using titanium isopropoxide (titanium precursor), boric acid (Boron precursor), sucrose (carbon source), and acetic acid (AcOH) as a solvent. The effect of boron source (trimethyl borate and boric acid) and B2O3/TiO2, C/B2O3 mole ratios of starting materials on the final phases has been studied. The progress of reactions was determined using thermal analysis (TGA‐DTA). The resultant powders were characterized by X‐ray diffraction (XRD) analysis and field‐emission scanning electron microscope (FESEM). XRD patterns confirmed the formation of TiB2, B4C, and TiC phases after heat treatment at 1450°C at mole ratio of B2O3/TiO2 = 4.5, C/B2O3 = 2.4. With increasing the content of boron oxide, the unwanted phases such as TiC and C were reduced. TiB2 and B4C composite powders (~5 µm diameter) containing residual carbon (<4 wt%) were synthesized using the mole ratio of B2O3/TiO2 = 10 and C/B2O3 = 1.9 at low temperature of 1450°C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Applied Ceramic Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.