Abstract
Transparent photocatalytic surfaces are of ever increasing importance for many applications on self-cleaning windows and tiles in everyday applications. Here, we report the formation and photocatalytic testing of a quasi-transparent thin and nanoporous titania films deposited on glass plates. Sputtered Ti thin films were anodized in fluoride-ion-containing neutral electrolytes to form optically semitransparent nanoporous films, which transformed to be completely transparent after thermal annealing. The nanoporous films were studied at different stages, such as before and after anodization, as well as after thermal annealing using scanning electron microscopy (SEM), X-ray diffraction (XRD), and UV-vis and Raman spectroscopy. It was observed that anodization at 20 V of high-temperature deposited titanium films resulted in regular nanopore films with pore diameters of 30 nm. Structural investigations on the transparent nanopore arrays reveal the presence of anatase phase TiO(2) even after annealing at 500 °C, which was confirmed by XRD and Raman spectroscopy measurements. The solar-light induced photocatalytic decomposition of stearic acid and photoconductivity characteristics of these nanoporous thin films are also presented.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.