Abstract
ABSTRACTNano-sized dispersions have been employed as precursor inks for the spray deposition of contacts to both Si and CdTe materials. In the case of Si, nano-sized Al particles (nano-Al) were dispersed and spray deposited onto p-type Si. Annealing above the eutectic temperature causes alloy formation yielding a p+ layer with p ∼ 10−4 Ω•cm. For CdTe, nano-sized Te particles (nano-Te) were dispersed and sprayed onto CdTe/CdS/SnO2/glass heterostructures. Contact to the CdTe layer occurred during a 30 min anneal in He (T = 215 to 255 °C). These solar cells were finished by spin-coating the Te layer with Ag paint and subsequently annealing in air (100 °C / 1 h). This approach produces solar cells with open circuit voltages (Voc) from 720 to 800 mV, short circuit current densities (Jsc) from 18 to 20 mA/cm2 and efficiencies up to 10.3%. The performance of these cells was similar to those produced using the standard NREL contact.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.