Abstract
BACKGROUND Tb3+doped hydroxyapatite was synthetized by the sol–gel technique, using amounts of the dopant source ranging from 2 to 12 wt%, with respect to the calcium former material. The solids were analyzed using several techniques in order to determine their structural, textural and optical properties. The photoactivity of the materials was tested in the degradation of 2,4-dichlorophenoxyacetic acid, under UV irradiation. RESULTS The analysis of the samples by X-ray diffraction, energy-dispersive X-ray spectroscopy and Fourier transform infrared spectroscopy indicates the formation of hydroxyapatite with calcium deficiency, with a stoichiometry close to the ideal in the sample doped with 10 wt% of terbium. The highest photoluminescence emission, production of •OH radicals under UV in the terephtalic acid reaction, as well as photocatalytic activity in the photodegradation of 2,4-dichlorophenoxyacetic acid (2,4-D) was found in the sample doped with 10 wt% of terbium, reaching almost total degradation and 95% of mineralization of the organic molecule, after 240 min irradiation. CONCLUSION Terbium doping during the synthesis of hydroxyapatite significantly improves its efficiency as photocatalyst. © 2017 Society of Chemical Industry
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Chemical Technology & Biotechnology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.