Abstract
We report the influence of boron doping concentration on the microstructure, electrical and optical properties of solution-processed zinc oxide (ZnO) thin films. The B doping concentration in the resultant solutions was varied from 0 to 5 at%, and the pH value of each synthetic solution was adjusted to 7.0. XRD measurements, SEM observations, and SPM examinations revealed that boron doping produced ZnO thin films consisting of a fine grain structure with a flat surface morphology. Moreover, ZnO thin films doped with B raised the texture coefficient along the (002) plane. All B-doped ZnO (ZnO:B) thin films exhibited higher transparency than that of the undoped ZnO thin film in the wavelengths between 350 and 650 nm. The optical band gap and Urbach energy of the ZnO:B thin films were higher than those of the undoped thin film. According to electrical transport characteristics, the 1% B-doped ZnO thin film exhibited the highest Hall mobility of 17.9 cm2/V s, the highest electron concentration of 1.2×1015 cm−3, and the lowest electrical resistivity of 2.2×102 Ω cm among all of the ZnO:B thin films.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.