Abstract
A 25 nm thick α‐alumina layer was deposited on a turbine‐grade silicon nitride by sol‐gel dip coating and subsequent heat treatment in air at 1200°C. This layer had a nanometer grain structure. Silicon nitride protected by this thin layer showed a significant improvement in oxidation resistance over its uncoated counterpart after 200 cyclic exposures in air at 1250°C. The oxide layer grown on the coated silicon nitride also exhibited superior surface morphology, compared with the uncoated silicon nitride.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.