Abstract
Nanocomposites of cobalt ferrite (CoFe2O4) and strontium ferrite (SrFe12O19) were synthesized with various weight ratios 1:1, 1:2, 1:4, 1:8 and 1:16, by chemical co-precipitation route with higher content corresponding to SrFe12O19. Dual phase refinement employed for the prepared composites and confirms the presence of independent CoFe2O4 and SrFe12O19 phases. The increasing weight fraction of SrFe12O19 in the prepared composites is in accordance with its increasing weight ratio. An increase in compressive strain in the composites was attributed to larger ionic radius of Sr+2 ions. The electrical behavior in the composites was described by Cole-Cole plots at 250 °C from 20 Hz-106 Hz. An increase in impedance with increasing weight ratio of SrFe12O19 was observed, due to creation of effective scattering centers. Conductivity mechanism was explained by Overlapping large polaron tunneling (OLPT) model. A decrease in dielectric constant with increasing frequency is due to decreasing space charge polarization, due to inability of charge carriers to follow the varying ac field. Decreasing trend in dielectric loss for the prepared composites confirms their utility in microwave absorption applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.