Soft-template-synthesis of hollow CuO/Co3O4 composites for pseudo-capacitive electrode: A synergetic effect on electrochemical performance

Abstract

Hollow CuO/Co3O4 hybrids, which inherited from its coordination polymer precursor consisting of sheets layer and nanoparticles layer composites, were synthesized and characterized by SEM, EDX, XRD and XPS. To assess its electrochemical capacitive performances, cyclic voltammetry, galvanostatic charging-discharging measurements and A.C. impedance tests were performed successively. The CuO/Co3O4 hybrids had higher capacitance and lower charge transfer resistance than bare Co3O4 nanostructures, revealing that it provided a protection layer and produced a synergistic effect due to the existence of CuO layer. The distinct synergistic effect could be further confirmed by endurance cycling tests. The capacitance of the CuO/Co3O4 hybrids was 111% retained after 500 cycles at a charging rate of 1.0Ag−1 and remained an intense growth trend after 2000 cycles at scan rate of 200mVs−1.