Abstract
It was demonstrated that smooth Nb surfaces could be obtained through buffered electropolishing (BEP) employing an electrolyte consisting of lactic, sulfuric, and hydrofluoric acids. Parameters that control the polishing process were optimized to achieve a smooth surface finish. The polishing rate of BEP was determined to be 0.646 μm/min which was much higher than 0.381 μm/min achieved by the conventional electropolishing (EP) process widely used in the superconducting radio frequency (SRF) community. Root mean square measurements using a 3D profilometer revealed that Nb surfaces treated by BEP were an order of magnitude smoother than those treated by the optimized EP process. The chemical composition of the Nb surfaces after BEP was analyzed by static and dynamic secondary ion mass spectrometry (SIMS) systems. SIMS results implied that the surface oxide structure of Nb might be more complicated than what usually believed and could be inhomogeneous. Preliminary results of BEP on Nb SRF single cell cavities and half-cells were reported. It was shown that smooth and bright surfaces could be obtained in 1800 s when the electric field inside a SRF cavity was uniform during a BEP process. This study showed that BEP is a promising technique for surface treatment on Nb SRF cavities to be used in particle accelerators.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.