Abstract
The influence of shot peening (SP) on high cycle fatigue (HCF) performance of smooth and notched specimens of hot-extruded ZK60 magnesium alloy was investigated and compared to that of hot-extruded and T5 aging-treated ZK60 magnesium alloy referred to as ZK60-T5. The increases in fatigue properties at the optimum Almen intensities were found to depend on the material states. In contrast to ZK60 alloy, higher smooth and notched fatigue properties for both unpeened and peened specimens were observed for ZK60-T5 alloy. Meanwhile, the improvement of fatigue life for notched specimen by SP was much more than that for the smooth specimen. The mechanism by which the compressive residual stress induced by SP resulted in the improvement of fatigue performance of smooth and notched specimens for ZK60 and ZK60-T5 alloys was discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.