Abstract
In this paper the smelting separation of high-alumina rich-manganese ore prepared with selective reduction and magnetic separation was proposed to produce the high carbon ferromanganese alloy (HCFeMn). The rational smelting separation parameters for high-alumina rich-manganese ore included the FC/O of 1.1, the smelting temperature of 1550?C, the smelting time of 60 min, and the basicity of 0.7. The smelting separation of high-alumina rich-manganese ore was achieved successfully. The content of Fe, C, Si and other impurities (P, S) were 12.13%, 6.73%, 0.17% and 0.14, 0.008, respectively. Especially, the recovery and the content of Mn reached 80.47% and 76.76%. The obtained high carbon ferromanganese alloy met the higher standard (FeMn78C8) of ferromanganese alloy, especially the content of Si P and S in the HCFeMn alloy was far below the standard value. Based on the SEM-EDS, XRD and thermodynamic calculation, the smelting and separation mechanisms of high-alumina rich-manganese ore was proposed to more effectively explain the effect of smelting parameters on slag/metal separation behaviors during the process of smelting HCFeMn alloys.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Mining and Metallurgy, Section B: Metallurgy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.