Abstract
Directionally solidified (DS) alloys with the nominal composition Ni-30 at. pct Fe-20 at. pct Al having eutectic microstructures were used to study slip transfer across interphase boundaries and dislocation nucleation at the interfacial steps. The slip transfer from the ductile second phase, γ(fcc) containing ordered γ′(L12) precipitates, to the ordered β(B2) phase and the generation of dislocations at the interface steps were interpreted using the mechanisms proposed for similar processes involving grain boundaries in polycrystalline single-phase materials. The criteria for predicting the slip systems activated as a result of slip transfer across grain boundaries were found to be applicable for interphase boundaries in the multiphase ordered Ni-Fe-Al alloys. The potential of tailoring the microstructures and interfaces to promote slip transfer and thereby enhance the intrinsic ductility of dislocation-density-limited intermetallic alloys is discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.