Abstract
H11 steel discs were tested by considering sliding/rolling friction under dry and lubricated conditions. The H11 discs were plasma nitrided at 500°C and 550°C for 9h. Wear tests were conducted at different slip ratios of 1.79%, 10.53% and 22.22%. The test loads were 100N, 150N and 200N. It was determined that plasma-nitrided H11 discs had a surface hardness of 1200–1400HV0.1. Plasma nitriding produced wear performance much higher than those of the un-nitrided but hardened samples. The wear mechanism of the plasma-nitrided discs was a mixture of adhesive wear, abrasive wear and plastic yielding.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.