Sliding friction and wear property of a-C and a-CN x coatings against SiC balls in water

Abstract

The amorphous carbon coatings with and without nitrogen ion incorporation (a-CN x and a-C) were deposited on Si (100) wafers and SiC disks by using ion beam assisted deposition, and their composition, structure and chemical bonding were characterized by using Auger electronic spectroscopy, Raman spectroscopy and X-ray photoelectron spectroscopy (XPS), respectively. The friction and wear properties of the a-CN x coatings sliding against SiC ball in water were investigated and compared with those of the a-C coatings. The worn surfaces of the a-CN x coatings were observed by scanning electron microscopy and analyzed by XPS. The micro-analysis results showed that the a-CN x coatings contained 12 at.% nitrogen and the sp 3 fraction in the a-CN x coatings was lower than that in the a-C coatings. There were two kinds of N 1s bonding states such as sp 2C N and sp 3C–N in the a-CN x coatings. The nanohardness of the a-CN x coatings was 29 GPa, lower than that of the a-C coatings (34 GPa). The tribological tests in water showed the friction coefficients of the a-CN x /SiC tribo-pair were in the range of 0.02–0.05, smaller than those of the a-C/SiC tribopair (0.03–0.07), and the specific wear rates of the a-C coating and SiC ball in the a-C/SiC tribo-pair were slight larger than those in the a-CN x /SiC tribopair. The XPS analysis on the a-CN x coatings' wear track showed that the surface nitrogen concentration of the a-CN x on the wear track decreased. This indicated that the nitrogen removal would change the wear track surface structure, and then improve the tribological properties of the a-CN x coatings in water.