Abstract
The study object was slag from the Balkhash copper smelter, obtained by re-melting anode mud containing nonferrous metals. The process flow for processing these slags includes sintering with Na2SO4, Na2CO3, and coal, followed by soda-alkaline leaching of the sinter and extraction of metals from the solution into marketable products. Since sintering is the main operation providing high selectivity, the composition of the products of this process was studied. The main transformations during sintering were determined, and the optimal parameters were identified. The structures of slags and sintered materials obtained during the experiments were studied by electron-probe microanalysis. Sintering was performed at 600–800 °C. The best results for sulphidization of slag components were obtained at 800 °C; a further increase in temperature leads to the smelting of sinter particles and slows down sulphidization. The optimal quantities of additives, based on the weight of the slag, are Na2SO4—45%, Na2CO3—15%, and reducing agent—41%, with a sintering time of 2 h. These conditions enable the sulphidization of non-ferrous metals in the slag to the entire depth of the polymetallic globules. The distinct concentration of harmful impurities (Ni, As, and Sb) was observed in the fine structure of the polymetallic globules.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.