Abstract
A detailed study on the influence of particle size varied from 8 nm to 53 nm on the structural and magnetic properties of La0.8Sr0.2MnO3−δ has been done. The unit cell volume increases and the microstrain in the compound shows peak formation as the particle size decreases. Nano particles of La0.8Sr0.2MnO3−δ exhibit superparamagnetism whose blocking temperature has a nonlinear and logarithmic decreasing tendency as function of particle size and applied magnetic field, respectively. Evidence of formation of a magnetically dead layer at the surface has been found and the ratio of the thickness of the dead layer to the particle size increases exponentially with particle size. The coercivity of the nanoparicles increases manifold as particle size varies from 53 nm to 21 nm. In the single domain region the coercivity exhibits a d−1.125 behavior. The temperature dependence of the saturation magnetization shows strong collective excitation due to the spin wave that varies as Tα with α>αbulk of 3/2. Thus the spin wave does not follow the Bloch law in the case of nano particles of La0.8Sr0.2MnO3−δ.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.