Size effects in concrete fracture – Part II: Analysis of test results

Abstract

This paper presents an analysis of the extensive experimental program aimed at assessing the influence of maximum aggregate size and specimen size on the fracture properties of concrete. Concrete specimens used were prepared with varying aggregate sizes of 4.75, 9.5, 19, 38, and 76 mm. Approximately 250 specimens varying in dimension and maximum aggregate size were tested to accomplish the objectives of the study. Every specimen was subjected to the quasi-static cyclic loading at a rate of 0.125 mm/min (0.005 in./min) leading to a controlled crack growth. The test results were presented in the form of load-crack mouth opening displacement curves, compliance data, surface measured crack length and crack trajectories as well as calculated crack length, critical energy release rate, and fracture toughness (G 1). There is a well pronounced general trend observed: G 1 increases with crack length (R-curve behavior). For geometrically similar specimens, where the shape and all dimensionless parameters are the same, the R-curve for the larger specimens is noticeably higher than that for the smaller ones. For a fixed specimen size, G 1 increases with an increase in the aggregate size (fracture surface roughness). For the same maximum aggregate size specimens, the apparent toughness increases with specimen size. It was clear that the rate of increase in G 1, with respect to an increase of the dimensionless crack length (the crack length normalized by the specimen width), increases with both specimen size and maximum aggregate size increase. The crack trajectory deviates from the rectilinear path more in the specimens with larger aggregate sizes. Fracture surfaces in concrete with larger aggregate size exhibit higher roughness than that for smaller aggregate sizes. For completely similar specimens, the crack tortuosity is greater for the larger size specimens. The crack path is random, i.e., there are no two identical specimens that exhibit the same fracture path, however, there are distinct and well reproducible statistical features of crack trajectories in similar specimens. Bridging and other forms of crack face interactions that are the most probable causes of high toughness, were more pronounced in the specimens with larger maximum size aggregates.