Abstract
Magnetic and ferroelectric properties are investigated for the polycrystalline Bi2Fe4O9 ceramics with different grain sizes (60–2000 nm) synthesized by a modified Pechini method. It shows that magnetic and ferroelectric properties are strongly dependent on the grain size. For the 60 nm samples, the magnetization curves exhibit a superimposed behavior of antiferromagnetic (AFM) with ferromagnetic (FM) component. As the grain size increases, FM component is suppressed and AFM interaction becomes dominant. Simultaneously, the Néel temperature (TN) shifts to high temperatures as the grain size increases. Compared with the 60 nm sample, ferroelectric hysteresis loops at room temperature are observed for the samples with large grain sizes (>200 nm) due to the reduced leakage currents. Among all samples, the 900 nm sample is found to have the smallest leakage current density (<10−6) and the largest remnant polarization (0.21 μC/cm2).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.