Abstract
Depending on the composition and structure of metallic glasses cells with the dimensions in the range from tenths nanometers to tenths micrometers were observed on the ductile fracture surface. The variation in dimple size was compared with the serrations presented on the loading curve at the nanoindentation of the metallic glasses with different compositions. Higher instantaneous deformation can be connected with simultaneous shearing at more suitable shear band configurations. The cell morphology with the various cell sizes is observed at the failure of the metallic glasses. At the failure of high strength metallic glasses, the cells are formed in short time due to the release of high amount of stored elastic energy. In this case the uniform cell morphology with the cell size of about 20 nm is observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.