Abstract
► Size and heat treatment effects of phase boundary composition Au 52.5− x Cd 47.5 Ag x were studied. ► The transformation temperature T 0 increases by quench. It is investigated that disordering of atoms and lattice defects make β-phase unstable. ► Downsizing sample decreased T 0 in β-phase, showed a tendency of increase in coexistent phase. ► Downsizing is supposed to make difficult nucleation for martensitic transformation. ► Increasing of surface ratio by downsizing of powder sample is estimated to make easy to transform from unstable β-phase to martensite phase. Size and heat treatment effects on martensitic transformation of phase boundary composition Au 52.5− x Cd 47.5 Ag x were studied. Au 52.5− x Cd 47.5 Ag x has coexistent phase of β-phase and α-phase of fcc structure at x > 42 at.%. The transformation temperature T 0 decreases as Au is substituted on Ag over phase boundary. T 0 increases by quench in both case of bulk and powder. This behavior is investigated that disordering of atoms and lattice defects make β-phase ( L 2 1 , B2 or bcc) unstable. Size effect was also inspected. Downsizing sample decreased the transformation temperature in β-phase. On the contrary, the transformation temperature of the coexistent phase showed a tendency of increase. Downsizing is supposed to make difficult nucleation for martensitic transformation because of reduction of β-phase ordered volume. Increasing of surface (disorder structure) ratio by downsizing of powder sample is estimated to make easy to transform from unstable β-phase to martensite phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.