Size control and shape evolution of single-twinned platinum nanocrystals in a room temperature colloidal synthesis

Milena Osmić,Joanna Kolny-Olesiak,Katharina Al-Shamery

doi:10.1039/c4ce01342e

Milena Osmić, Joanna Kolny-Olesiak + Show 1 more

Open Access

https://doi.org/10.1039/c4ce01342e

Copy DOI

Journal: CrystEngComm	Publication Date: Sep 5, 2014
Citations: 12	License type: cc-by

Affiliation: Carl von Ossietzky University of Oldenburg

Abstract

Platinum nanocrystals in the size range of a few nanometers are especially interesting candidates for catalytic applications. We present an easy, low-temperature procedure, which allows for a precise size control of this material. Uniform platinum nanoparticles were obtained by reduction of platinum(IV)chloride with tetrabutylammonium borohydride in toluene solution at room temperature. Dodecylamine served as a ligand. The size of the resulting particles could be controlled in the range between 2 and 5 nm by slow addition of platinum monomers and the reducing agent to preformed 2 nm seeds. Furthermore, particles with a tetrapod shape could be synthesized. In contrast to the usual kinetic control leading to the formation of elongated structures, the analysis of the growth process of the tetrapods suggests a reaction-controlled growth process. Their structure was investigated by powder X-ray diffraction and high-resolution electron microscopy, which revealed that two branches of the tetrapods grow along the 〈111〉 direction, while the other two show growth in the 〈220〉 direction. This uncommon shape of the tetrapods is attributable to the presence of a twin defect parallel to the 〈220〉 direction. Thus, the method presented in the article allows for the formation of platinum particles with a single twin defect with a high yield.

Highlights

Small platinum nanoparticles with diameters of about 2 nm can be synthesized in organic solution at room temperature and under atmospheric pressure by reduction of platinumIJIV)chloride with tetrabutylammonium borohydride with dodecylamine as a ligand.[35]
Their structure was investigated by powder X-ray diffraction and highresolution electron microscopy, which revealed that two branches of the tetrapods grow along the 〈111〉 direction, while the other two show growth in the 〈220〉 direction
CrystEngComm particles synthesized with this method are rather limited, and attempts to grow larger particles by increasing the concentration of the precursors or by instantaneous injection of additional monomers to preformed particles do not lead to the expected outcome but result, e.g., in the formation of nanowires or the formation of additional small particles.[30]

Summary

Introduction

Small platinum nanoparticles with diameters of about 2 nm can be synthesized in organic solution at room temperature and under atmospheric pressure by reduction of platinumIJIV)chloride with tetrabutylammonium borohydride with dodecylamine as a ligand.[35]. The size of the resulting particles could be controlled in the range between 2 and 5 nm by slow addition of platinum monomers and the reducing agent to preformed 2 nm seeds.

Results

Conclusion