Abstract
The low-cost, low-density ceramic proppants with high breakage resistance were successfully prepared from low-grade bauxite (59.9wt%Al2O3) partially replaced by purple sand via solid state sintering method. The phase evolution and microstructure of the ceramic proppants sintered at different temperatures were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results showed that with the increase of sintering temperature, the crystalline phases were transferred from sillimanite to mullite and corundum, and glass phase was generated. When sintered at the proper temperature of 1440°C, the close integration of mullite and corundum bonded by the proper liquid phase was observed, and the obtained proppant presents the apparent density of 2.98g/cm3, bulk density of 1.64g/cm3 and lowest breakage ratio of 7.8% under 52MPa closed pressure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.