Sintering of high-entropy nanoparticles obtained by polyol process: A case study of (La0.2Y0.2Nd0.2Sm0.2Gd0.2)2Ce2O7-δ

Abstract

High-entropy (HE) ceramics nanoparticles have received much attention due to their interesting properties. However, very limited studies have been conducted on their sintering. Here, we report the sintering behavior of HE A2B2O7 type rare earth oxide nanoparticles obtained by polyol process. HE cerate (HECe) (La0.2Y0.2Nd0.2Sm0.2Gd0.2)2Ce2O7-δ is chosen as an exemplary case, which is considered as a good candidate for thermal insulation. HECe nanoparticles with size of 2.6–7.1 nm can be synthesized through polyol process followed by annealing in air at 300–700 °C. HECe nanoparticle compact can be densified by directly sintering at 1500 °C. The sintering temperature could be further decreased using a two-step sintering process, i.e., 1500 °C 5 min-1300 °C 5 h. Our results show that fine particle and abundant oxygen vacancies probably dominate the densification process. By controlling the sintering regime, we can tune the microstructure of HECe ceramics and thermal conductive properties accordingly.