Abstract
Sc3+ substituted M-type ferrites are effective microwave magnetic materials with a ferromagnetic resonance frequency in the range of 20 GHz–50 GHz. We report on the fabrication of oriented ferrite thick films as microwave components for application in the Ka-band at 30 GHz. Films of BaFe11.5.Sc0.5O19 were prepared by screen-printing on alumina substrates, drying in an external magnetic field, and sintering at 900 °C. Low-temperature sintering is achieved through use of a mixed BBSZ/CuO sintering aid. A strong anisotropy of the sintered ferrite films is revealed by XRD analysis. Microwave properties of the films were determined in a coplanar waveguide setup. The ferromagnetic resonance frequency of the films is at 30 GHz and the textured films possess good nonreciprocal properties which scale with film thickness. The films were tested in a Y-junction circulator, and represent promising materials for self-biased microwave components fabricated in thick film technology.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.