Sintering, microstructural development, and electrical properties of gadolinia -doped ceria electrolyte with bismuth oxide as a sintering aid

Abstract

A considerable reduction (≥250 °C) in the sintering temperature, enhancement of the sintering density, and a slight improvement of the electrical properties, can be achieved by using bismuth oxide in the range of 0.2 to 2 wt.%, as a sintering aid for gadolinia-doped ceria (GDC) ceramic electrolytes. Dilatometric experiment (CHR) and SEM observations indicate that a liquid phase-assisting sintering mechanism contributes to the improvement in sintering density for bismuth oxide concentrations exceeding 0.5 wt.%. The addition of small amount of Bi 2O 3 ≤0.5 wt.% also results in the achievement of highly dense ceramic bodies (≥99% of theoretical density) after sintering at 1200 °C for 4 h, which indicates that the addition of Bi 2O 3 to gadolinia-doped ceria promoted the sintering process by a cooperating volume diffusion-liquid phase-assisting mechanism. Based on the lattice constant data, the solid solubility limit of Bi 2O 3 in gadolinia-ceria is, probably, lower than 1.0 wt.%. Grain size also increased with increasing Bi 2O 3 content up to 0.5 wt.% and then it decreased with further addition of Bi 2O 3. The addition of the smaller amounts of bismuth oxide, i.e., ≤1.0 wt.% Bi 2O 3 slightly enhanced the total ionic electrical conductivity of the gadolinia-doped ceria electrolyte. The sintering temperature strongly influenced the electrical conductivity of the doped-GDC ceramics. The best sample was that containing 1.0 wt.% Bi 2O 3 sintered at 1400 °C for 2 h which had an ionic electrical conductivity of 4 S m −1 at 700 °C, and an activation energy of 0.58 eV for the oxide-ion conduction process in air.