Abstract
This work investigates the effects of time dependency for isothermal sintering on additive manufactured Ni–Mn–Ga magnetic shape memory alloys. Binder jetting additive manufacturing was used to produce Ni–Mn–Ga parts from pre-alloyed powders. Additive manufacturing via the binder jetting technique produces parts with intrinsic porosities, based on the morphology of the source material. The Ni–Mn–Ga parts printed in this study using the binder jetting method possessed average densities of ~ 46% before sintering. These samples were sintered at 1353 K in increments of 10 h up to 50 h. Based on this temperature and time frame, (1) microstructural evolution, (2) crystallographic phase analysis, (3) transformation behaviors, and (4) thermal–physical properties were investigated. The additive manufactured Ni–Mn–Ga samples exhibited increases in densities, from ~ 74 to ~ 83% due to solid-state diffusion mechanisms. X-ray diffraction reveals that all of the additive manufactured samples have the 5 M martensitic phase at room temperature. Reversible martensitic transformation temperatures were recorded during heating and cooling cycles through differential scanning calorimetry, which indicate austenitic phase transformations occurring slightly above ambient temperatures. Additionally, analysis of the heating and cooling cycles prescribes that the entropy and Gibb’s energies decrease over the reversible martensitic transformations as sintering time increases. It is envisioned that this study will support a more synergistic manufacturing process between binder jetting additive manufacturing and post-heat treatment processes for Ni–Mn–Ga shape memory alloys.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.