Abstract
The sintering behavior and dielectric properties of the monoclinic zirconolite-like structure compound Bi 2(Zn 1/3Nb 2/3) 2O 7 (BZN) and Bi 2(Zn 1/3Nb 2/3− x V x ) 2O 7 (BZNV, x = 0.001) sintered under air and N 2 atmosphere were investigated. The pure phase were obtained between 810 and 990 °C both for BZN and BZNV ceramics. The substitution of V 2O 5 and N 2 atmosphere accelerated the densification of ceramics slightly. The influences on microwave dielectric properties from different atmosphere were discussed in this work. The best microwave properties of BZN ceramics were obtained at 900 °C under N 2 atmosphere with ɛ r = 76.1, Q = 850 and Q f = 3260 GHz while the best properties of BZNV ceramics were got at 930 °C under air atmosphere with ɛ r = 76.7, Q = 890 and Q f = 3580 GHz. The temperature coefficient of resonant frequency τ f was not obviously influenced by the different atmospheres. For BZN ceramics the τ f was −79.8 ppm/°C while τ f is −87.5 ppm/°C for BZNV ceramics.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.