Abstract
The effect of phosphorus additions on the structure, microstructure and dielectrics properties of the Pb0.98Ca0.02[(Zr0.52Ti0.48)0,98(Cr3+0.5, Ta5+0.5)0,02]1-xPx O3 (x ranged from 0.01 to 0.12) ceramics have been investigated. All of the samples were prepared by a high-temperature solid-state reaction technique. AFM analysis of the compounds suggests that the average grain size increases with increasing sintering temperature which is characteristic of a ceramic material. Until that it reaches maximum values for the simple doped with 4 Wt. % of P2O5 at a sintering temperature of 1050°C. Dielectric studies of the compounds as a function of frequency (from 1 to 200 KHz) sintered at different sintering temperatures (1000, 1050, 1100, 1150 and 1180° C) show that the compounds undergo a phase transition of diffuse type. The transition temperature shifts towards higher side with increase in frequency a typical characteristic of a relaxor material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.