Abstract
Calcia stabilized zirconia(CSZ) ceramics were prepared with 7wt% calcia-stabilized zirconia powder by pressureless sintering technology. The crystal phases of the sintered samples were studied by X-ray diffraction(XRD) and Raman spectroscopy techniques, and the microstructures of the fracture surfaces were observed by scanning electron spectroscopy(SEM). The phase compositions and the lattice parameters of cubic calcia-stabilized zirconia were calculated by XRD patterns. As the sintering temperature increasing from 1400 °C to 1600 °C, the monoclinic zirconia content decreases gradually, finally all monoclinic phase transforms to cubic calcia-stabilized zirconia, which is determined to be Ca0.134Zr0.866O1.866. It is revealed that monoclinic zirconia is the main factor causing minute cracks on the surface of sintered samples, and the combination of the XRD patterns and Raman spectra is an effective way to research the phase transformations of zirconia.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.