Abstract
AlZrC 2 powder prepared by solid-state reaction was sintered using a pulse electric current sintering technique in a temperature range from 1700 to 2000°C under the pressure of 40 MPa in vacuum for 5 min. The density and mechanical properties of the sintered AlZrC 2 monolith were estimated. As heating temperature increased, the density of the AlZrC2 monolith increased and the mechanical properties were improved. The bulk density of the AlZrC 2 monolith sintered at 2000°C was 5.12 g/cm 3 . The maximum values of the fracture strength and Vickers' hardness were 380 MPa and 11.1 GPa, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.