Abstract
Sintered reaction‐bonded silicon nitride (SRBSN) materials were prepared from a high‐purity Si powder doped with Y2O3 and MgO as sintering additives by nitriding at 1400°C for 8 h and subsequently postsintering at 1900°C for various times ranging from 3 to 24 h. Microstructures and phase compositions of the nitrided and the sintered compacts were characterized. The SRBSN materials sintered for 3, 6, 12, and 24 h had thermal conductivities of 100, 105, 117, and 133 W/m/K, and four‐point bending strengths of 843, 736, 612, and 516 MPa, respectively. Simultaneously attaining thermal conductivity and bending strength at such a high level made the SRBSN materials superior over the high‐thermal conductivity silicon nitride ceramics that were prepared by sintering of Si3N4 powder in our previous works. This study indicates that the SRBSN route is a promising way of fabricating silicon nitride materials with both high thermal conductivity and high strength.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Applied Ceramic Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.