Time-resolved small-angle X-ray scattering (TR-SAXS) studies of the structural changes in a block copolymer after a temperature jump are reported. The sample used was a polystyrene-block-poly(ethylene-alt-butylene)-block-polystyrene (SEBS) triblock copolymer, which has a number-average molecular weight of 54000 g mol−1and a volume fraction of polystyrene of 0.227. The film specimen was prepared by the solution-cast method using a selective solvent. The as-cast specimen with lamellar microdomains underwent the temperature jump from 363 to 403 K and the morphological transition from lamellae to cylinders was observed as a function of time by the TR-SAXS technique. The singular value decomposition (SVD) analysis was performed on the scattering profiles. This analysis strongly suggested the existence of a third basis component of the X-ray scattering profiles, thus supporting that there is an intermediate state during the transition from lamellae to cylinders.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.