Abstract
To prevent dendrite growth and hydrogen evolution reaction, directional epitaxial growth of Zn2+ ions on Zn anode, especially along the lowest‐surface‐energy Zn (0002) plane, is pursued for highly reversible zinc metal batteries (ZMBs). However, designing single Zn (0002) exposed anodes for sustained uniaxial crystalline orientation of Zn electroplating faces challenges. Herein, we propose an anode engineering that utilizes a low lattice mismatch substrate and ordered Zn2+ migration channels to modify Zn anodes with single (0002) surface exposure and sustainable Zn‐oriented growth, yielding highly reversible ZMBs. A vapor‐deposited metal‐organic framework Cu3(C6O6)2 film on brass foil shows low lattice mismatch (4.24%) with electrodeposited Zn anodes, enabling the exposure of a single (0002) plane. Furthermore, the low desolvation energy (−1.36 eV) between solvated Zn2+ ions and the ordered porous Cu3(C6O6)2 film guides sustainable Zn‐oriented nucleation along the Zn (0002) surface. Consequently, the Zn||Zn cells with brass‐Cu3(C6O6)2 substrate shows a high average Coulombic efficiency of 99.55% after 4,000 cycles at 10 mA cm−2. This work provides a new window to design highly reversible Zn metal anode with a single‐exposed Zn (0002) plane and sustainable oriented growth for emerging ZMBs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.