Abstract
Single crystal of novel orange-red emission CaAl2Si4N8:Eu2+ phosphor was grown by our original vapor phase technique, and the precise crystal structure was investigated for the first time by single crystal X-ray diffraction analysis. The crystal structure of CaAl2Si4N8:Eu2+ single crystal was verified to be an α-Si3N4-type trigonal structure (space group P31c) with a = 0.79525(9) nm, c = 0.57712(8) nm, and z = 2. The Ca atoms were coordinated to seven nitrogen atoms and located in the three-dimensional framework formed by (Al, Si)N4 tetrahedra. The single-crystal CaAl2Si4N8:Eu2+ phosphors exhibited a broad reddish-yellow emission with a peak at 600 nm under near-UV and blue light excitation. When increasing the temperature up to 150 °C, the emission intensity of the CaAl2Si4N8:Eu2+ phosphor decreased to 88% of the initial value at 25 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.