Abstract
Simultaneous hardening and toughening effects were found for WC–(nanoWC–Co) with microWC strengthening particles in nanoWC–Co cermet matrix. The high microhardness of 1683 ± 176 Hv comparable to that of nanoWC–12Co was attributed to the hardening effect from both microWC particles and nanoWC dispersion in the Co binder phase. The high fracture toughness of 18.9 ± 4.0 MPa m1/2, comparable to that of microstructured WC–12Co, resulted from the larger area of the bimodal-sized fracture surface morphology and the crack bridging due to the microsized strengthening WC particles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.