Abstract
Coarse Al-Si alloy is produced from bauxite via carbon electro-thermal reduction method. Silicon and iron-rich phases are two main detrimental impurities in coarse Al-Si alloy, and they can be simultaneously removed by adding Mn under the electromagnetic field. We focus on the influence of different Mn additions, dropping rates, and current intensity on the simultaneous removal efficiency of Si and Fe. Experimental results show that as mole ratio of Mn/Fe reaches more than 0.8, the morphology of iron-rich phases together with silicon changed from harmful acicular-like to the contributing bulks, concentrated at the bottom of Al-Si alloy as intermetallic compounds. Furthermore, when Mn/Fe reaches 1.2 and a lower dropping rate (5 to 25 μm/s) is adopted, both Si and Fe contents in the Al-Si alloy decreased drastically after electromagnetic directional solidification process, reaching 11.42 and 0.4 pct, respectively, with a desirable Fe removal efficiency of 91 pct. Finally, the principle of simultaneously separating Si and removing iron-rich phases from Al-Si alloy is studied deeply.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.