Abstract
The combined effects of compact TiO2 (c-TiO2 ) electron-transport layer (ETL) are investigated without and with mesoscopic TiO2 (m-TiO2 ) on top, and without and with an iodine-terminated silane self-assembled monolayer (SAM), on the mechanical behavior, opto-electronic properties, photovoltaic (PV) performance, and operational-stability of solar cells based on metal-halide perovskites (MHPs). The interfacial toughness increases almost threefold in going from c-TiO2 without SAM to m-TiO2 with SAM. This is attributed to the synergistic effect of the m-TiO2 /MHP nanocomposite at the interface and the enhanced adhesion afforded by the iodine-terminated silane SAM. The combination of m-TiO2 and SAM also offers a significant beneficial effect on the photocarriers extraction at the ETL/MHP interface, resulting in perovskite solar cells (PSCs) with power-conversion efficiency (PCE) of over 24% and 20% for 0.1 and 1cm2 active areas, respectively. These PSCs also have exceptionally long operational-stability lives: extrapolated T80 (duration at 80% initial PCE retained) is ≈18000 and 10000h for 0.1 and 1cm2 active areas, respectively. Postmortem characterization and analyses of the operational-stability-tested PSCs are performed to elucidate the possible mechanisms responsible for the long operational-stability.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.