The deformation, damage and failure behaviors of 17vol.% SiCp/2009Al composite were studied by microscopic finite element (FE) models based on a representative volume element (RVE) and a unit cell. The RVE having a 3D realistic microstructure was constructed via computational modeling technique, in which an interface phase with an average thickness of 50nm was generated for assessing the effects of interfacial properties. Modeling results showed that the RVE based FE model was more accurate than the unit cell based one. Based on the RVE, the predicted stress-strain curve and the fracture morphology agreed well with the experimental results. Furthermore, lower interface strength resulted in lower flow stress and ductile damage of interface phase, thereby leading to decreased elongation. It was revealed that the stress concentration factor of SiC was ∼2.0: the average stress in SiC particles reached ∼1200MPa, while that of the composite reached ∼600MPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.